Mechanical properties	Test Condition	BASF GERMANY/B3ZG8
Impact strength of cantilever beam gap	30℃，干	14 KJ/m
Charpy Notched Impact Strength	+23℃，干/湿	100/105 KJ/m
Impact Strength	+23℃，干/湿	18/25 J
Tensile modulus	干/湿	11200/7200 Mpa
Charpy Notched Impact Strength	30℃，干	90 KJ/m
Fracture stress (V=50mm/min)	干/湿	165/115 Mpa
Impact strength of cantilever beam gap	+23℃，干/湿	22 KJ/m
ball-indentation hardness	干/湿	190/110 Mpa
Charpy Notched Impact Strength	30℃，干/湿	20 KJ/m
bending strength	干/湿	270/200 Mpa
elongation at break	干/湿，V=50mm/min	4/7 %
Tensile yield stress (V=50mm/min)	干/湿	165/115 Mpa

Electrical performance	Test Condition	BASF GERMANY/B3ZG8
dielectric constant	1MHz，干/湿	4/5.3
Compared to the Leakage Traceability Index (CTI)	干/湿	CTI 550
dielectric strength	K20/P50，干/湿	80/70 KV/mm
loss angle	1MHz，干/湿	0.019/0.13
Surface Resistivity	干/湿	10 Ω
Volume resistivity	干/湿	10 Ω.cm

Thermal performance	Test Condition	BASF GERMANY/B3ZG8
TEMPERATURE	在20000h/5000h，后拉伸强度下降50%时	110/120 °C
Heat distortion temperature	1.8MPa负荷，干态，HDT	210 °C
thermal conductivity	干态	0.32 W/(m.K)
Heat distortion temperature	0.45MPa负荷，干态，HDT	220 °C
maximum service temperature		180 °C
Linear coefficient of thermal expansion	（23-80）℃，干态	1-2/5-6