PA6 PA NE 50-1 Poly Plastic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Poly Plastic/ PA NE 50-1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 20°C | 60 kJ/m² | |
| Charpy Notched Impact Strength | 20°C | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Poly Plastic/ PA NE 50-1 |
|---|---|---|---|
| Flexural modulus | 23°C | 12500 MPa | |
| Tensile strain | 断裂 | 3.0 % | |
| bending strength | 260 MPa | ||
| tensile strength | 屈服 | 185 MPa |
| Electrical performance | Test Condition | Test Method | Poly Plastic/ PA NE 50-1 |
|---|---|---|---|
| Volume resistivity | --3 | 1E+15 ohms·cm | |
| --2 | 1E+17 ohms·cm | ||
| Surface Resistivity | --3 | 1E+13 ohms | |
| --2 | 1E+15 ohms | ||
| dielectric strength | --3 | 14to19 kV/mm | |
| --2 | 22to25 kV/mm |
| physical property | Test Condition | Test Method | Poly Plastic/ PA NE 50-1 |
|---|---|---|---|
| Shrinkage rate | 0.25to0.40 % | ||
| density | 1.56 g/cm³ | ||
| Water absorption rate | 饱和,23°C | 5.5 % | |
| 23°C,24hr | ISO 62 | 0.80 % | |
| 平衡,23°C,50%RH | 1.8 % |
| Thermal performance | Test Condition | Test Method | Poly Plastic/ PA NE 50-1 |
|---|---|---|---|
| melting temperature | 219 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | 205 °C |