POM KFX-1004 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical components,Laptop case
High temperature resistan,Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1004 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 590 J/m |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1004 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 162 °C |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1004 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.3 % |
| tensile strength | 断裂 | ASTM D638 | 108 Mpa |
| flexural modulus | ASTM D790 | 8200 Mpa | |
| bending strength | ASTM D790 | 186 Mpa |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/KFX-1004 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Temperature in the middle of the barrel | 195 to 205 °C | ||
| Temperature at the rear of the barrel | 175 to 190 °C | ||
| Processing (melt) temperature | 200 to 215 °C | ||
| mold temperature | 80 to 110 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 210 to 220 °C | ||
| Back pressure | 0.200 to 0.300 Mpa |