PEEK AV-651 BK SOLVAY USA
AVASPIRE®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTMD256 | 无断裂 |
| hardness | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 94 |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| Dissipation Factor | 1kHz | ASTM D150 | 1E-03 |
| 60Hz | ASTM D150 | 1E-03 | |
| dielectric constant | 60Hz | ASTM D150 | 3.10 |
| Volume resistivity | ASTM D257 | 5E+17 ohms·cm | |
| Surface Resistivity | ASTM D257 | >1.9E+17 ohms | |
| dielectric constant | 1kHz | ASTM D150 | 3.12 |
| Dissipation Factor | 1MHz | ASTM D150 | 4E-03 |
| dielectric strength | 3.00mm | ASTM D149 | 16 KV/mm |
| dielectric constant | 1MHz | ASTM D150 | 3.10 |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| elongation | 断裂5 | ASTM D638 | >40 % |
| Tensile modulus | -- | ISO 527-2/1A/1 | 3200 Mpa |
| --5 | ASTM D638 | 3000 Mpa | |
| Flexural modulus | -- | ISO 178 | 3200 Mpa |
| bending strength | -- | ISO 178 | 127 Mpa |
| tensile strength | --5 | ASTM D638 | 87.0 Mpa |
| elongation | 屈服 | ISO 527-2/1A/50 | 5.7 % |
| bending strength | -- | ASTM D790 | 124 Mpa |
| elongation | 屈服5 | ASTM D638 | 6.2 % |
| shear strength | ASTM D732 | 78.0 Mpa | |
| elongation | 断裂 | ISO 527-2/1A/50 | >40 % |
| Flexural modulus | -- | ASTM D790 | 3100 Mpa |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 89.0 Mpa |
| compressive strength | ASTM D695 | 112 Mpa |
| flammability | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-0 |
| 1.6mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| melt viscosity | 400°C,1000sec^-1 | ASTM D3835 | 240 Pa·s |
| physical property | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| melt mass-flow rate | 400°C/2.16kg | ASTM D1238 | 25 g/10min |
| Shrinkage rate | TD:3.18mm | ASTM D955 | 1.0-1.2 % |
| Water absorption rate | 24hr | ASTM D570 | 0.20 % |
| Shrinkage rate | MD:3.18mm | ASTM D955 | 0.70-0.90 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/AV-651 BK |
|---|---|---|---|
| thermal conductivity | ASTME1530 | 0.24 W/m/K | |
| Heat distortion temperature | 1.8MPa,退火,3.20mm，HDT | ASTM D648 | 190 °C |
| Linear coefficient of thermal expansion | MD：-50到50°C | ASTME831 | 4.7E-05 cm/cm/°C |
| specific heat | 50°C | DSC | 1310 J/kg/°C |
| 200°C | DSC | 1820 J/kg/°C | |
| melting temperature | ASTM D3418 | 345 °C | |
| Glass Transition Temperature | ASTM D3418 | 158 °C |