PC FR3020 Covestro - Polycarbonates
--
Thin walled components
Filler, mineral filler, 5, 0%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Covestro - Polycarbonates/ FR3020 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 11 kJ/m² |
| Electrical performance | Test Condition | Test Method | Covestro - Polycarbonates/ FR3020 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 kV/mm |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.00 |
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.10 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Surface Resistivity | IEC 60093 | 1E+16 ohms | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 5E-03 |
| 23°C,1MHz | IEC 60250 | 7E-03 |
| Mechanical properties | Test Condition | Test Method | Covestro - Polycarbonates/ FR3020 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/50 | 65.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 4.0 % |
| 断裂,23°C | ISO 527-2/50 | >30 % | |
| tensile strength | 断裂,23°C | ISO 527-2/50 | 50.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 3200 MPa |
| flammability | Test Condition | Test Method | Covestro - Polycarbonates/ FR3020 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | 5VA | |
| 2.0mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | Covestro - Polycarbonates/ FR3020 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| MeltViscosity | 260°C | ISO 11443-A | 200 Pa·s |
| Shrinkage rate | TD:240°C,3.00mm | ISO 2577 | 0.40to0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.50 % | |
| Shrinkage rate | MD:240°C,3.00mm | ISO 2577 | 0.40to0.60 % |
| Melt volume flow rate | 240°C/5.0kg | ISO 1133 | 20.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | Covestro - Polycarbonates/ FR3020 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 103 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 95.0 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 85.0 °C |
| vicat | -- | ISO 306/B50 | 101 °C |