POM 500CL NC010 DUPONT NETHERLANDS
Delrin®
Automotive Applications、Fitness equipment、Engine parts
High rigidity、heat-resisting、High impact resistance、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 9.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 350 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 290 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO2039-2 | 92 |
| R计秤 | ISO2039-2 | 120 |
| Supplementary Information | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| Emission | VDA275 | <8.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 6.00 µgC/g |
| Mechanical properties | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| Nominal tensile fracture strain | ISO527-2 | 25 % | |
| Tensile stress | 屈服 | ISO527-2 | 67.0 Mpa |
| Tensile strain | 屈服 | ISO527-2 | 15 % |
| Tensile modulus | ISO527-2 | 3100 Mpa | |
| Flexural modulus | ISO178 | 2900 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| CTI | IEC60112 | 600 V | |
| 1MHz | IEC60250 | 4.10 | |
| 100Hz | IEC60250 | 4.20 |
| flammability | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB |
| 1.5mm | UL94 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| Burning rate 3 | 1.00mm | ISO3795 | 28 mm/min |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB |
| 1.5mm | IEC60695-11-10,-20 | HB |
| physical property | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.8 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 1.0 % |
| melt mass-flow rate | ISO1133 | 15 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 12.0 cm3/10min |
| Shrinkage rate | MD | ISO294-4 | 1.9 % |
| density | ISO1183 | 1.41 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.25 % |
| Thermal performance | Test Condition | Test Method | DUPONT NETHERLANDS/500CL NC010 |
|---|---|---|---|
| TD | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| AnnealingTemperature | 160 °C | ||
| vicat | ISO306/B50 | 160 °C | |
| melting temperature | ISO11357-3 | 178 °C | |
| MD | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| AnnealingTime-Optional | 30.0 min/mm | ||
| Heat distortion temperature | 1.8MPa,未退火 | ISO75-2/A | 90.0 °C |
| 0.45MPa,未退火 | ISO75-2/B | 158 °C |