film	Test Condition	Test Method	LOTTE KOREA/UF414
tensile strength	MD : 断裂, 40 µm, 吹塑薄膜	ASTM D882	39.2 Mpa
Falling hammer impact	40 µm, 吹塑薄膜	ASTM D1709	140 g
Elmendorf Tear Strength?2	TD : 40.0 µm	ASTM D1922	9.0 g/µm
Film thickness - tested			40 µm
elongation	MD : 断裂, 40 µm, 吹塑薄膜	ASTM D882	780 %
tensile strength	TD : 断裂, 40 µm, 吹塑薄膜	ASTM D882	34.3 Mpa
Elmendorf Tear Strength?2	MD : 40.0 µm	ASTM D1922	5.0 g/µm
elongation	TD : 断裂, 40 µm, 吹塑薄膜	ASTM D882	800 %

optical performance	Test Condition	Test Method	LOTTE KOREA/UF414
Haze ratio	40.0 µm, 吹塑薄膜	ASTM D1003	12 %
gloss	45°, 40.0 µm, 吹塑薄膜	ASTM D2457	72

physical property	Test Condition	Test Method	LOTTE KOREA/UF414
density		ASTM D1505	0.920 g/cm³
melt mass-flow rate	190°C/2.16 kg	ASTM D1238	2.0 g/10 min