Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
GPPS GP550N FORMOSA NINGBO
TAIRIREX®
--
currency、high molecular weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FORMOSA NINGBO/GP550N |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 18 J/m |
| 23°C,6.35mm | ISO 180 | 18 J/m |
| Supplementary Information | Test Condition | Test Method | FORMOSA NINGBO/GP550N |
|---|---|---|---|
| Residual Monomer | <700 ppm |
| Mechanical properties | Test Condition | Test Method | FORMOSA NINGBO/GP550N |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| bending strength | 23°C | ISO 178 | 98.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 51.0 Mpa |
| bending strength | 23°C | ASTM D790 | 98.1 Mpa |
| Flexural modulus | 23°C | ISO 178 | 3330 Mpa |
| 23°C | ASTM D790 | 3330 Mpa | |
| tensile strength | 23°C | ASTM D638 | 51.0 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 2.0 % |
| flammability | Test Condition | Test Method | FORMOSA NINGBO/GP550N |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FORMOSA NINGBO/GP550N |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 2.3 g/10min |
| 200°C/5.0kg | ISO 1133 | 2.3 g/10min | |
| density | ASTM D792 | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | FORMOSA NINGBO/GP550N |
|---|---|---|---|
| vicat | ASTM D1525 | 104 °C | |
| ISO 306/B | 104 °C | ||
| Heat distortion temperature | 1.8MPa,Annealed,3.18mm，HDT | ISO 75-2/A | 95.0 °C |
| 1.8MPa,Annealed,3.18mm，HDT | ASTM D648 | 95.0 °C |