PP 37T1020U-00900 SABIC INNOVATIVE SHANGHAI
SABIC®
Electrical applications,electromagnetic shielding
Glass fiber reinforced,Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/37T1020U-00900 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 52 J/m |
| Suspended wall beam without notch impact strength | 23°C,3.20mm | ASTM D4812 | 850 J/m |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 1.7 kJ/m² |
| 23°C | ISO 180/1A | 3.4 kJ/m² | |
| 0°C | ISO 180/1A | 3.5 kJ/m² | |
| InstrumentedDartImpact | 23°C,EnergyatPeakLoad | ASTM D3763 | 3.93 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/37T1020U-00900 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 71 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/37T1020U-00900 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2760 Mpa | |
| ASTM D638 | 2450 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 28.0 Mpa |
| elongation | 断裂 | ASTM D638 | 33 % |
| 屈服 | ASTM D638 | 3.7 % | |
| Flexural modulus | 50.0mm跨距4 | ISO 178 | 2840 Mpa |
| 50.0mm跨距5 | ASTM D790 | 2350 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 17.0 Mpa |
| 屈服 | ASTM D638 | 25.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 45 % |
| tensile strength | 断裂 | ISO 527-2/1A/50 | 25.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.5 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/37T1020U-00900 |
|---|---|---|---|
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 13 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/37T1020U-00900 |
|---|---|---|---|
| vicat | ISO 306/A50 | 145 °C | |
| Heat distortion temperature | 0.45MPa,Unannealed，HDT | ISO 75-2/B | 110 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 116 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 6.7E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,Unannealed，HDT | ISO 75-2/A | 69.0 °C |
| Linear coefficient of thermal expansion | TD：-30to100°C | ISO 11359-2 | 1.3E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 60.0 °C |