PP 2035G STYRON US
DOWLEX™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| elongation at break | ASTM D4649 | 340 % | |
| tensile strength | MD:断裂,23µm,挤塑薄膜 | ASTM D882 | 26.0 Mpa |
| Film tensile performance - load on pallet | ASTM D4649 | 13000 g | |
| elongation | MD:断裂,23µm,挤塑薄膜 | ASTM D882 | 520 % |
| Film tensile performance - improve tear strength - @ maximum tensile rate | ASTM D4649 | 47 % | |
| Elmendorf tear strength | MD:23µm,铸造薄膜 | ASTM D1922 | 250 g |
| TD:23µm,铸造薄膜 | ASTM D1922 | 490 g | |
| Dart impact | 23µm,铸造薄膜 | ASTM D1709A | 120 g |
| tensile strength | TD:断裂,23µm,挤塑薄膜 | ASTM D882 | 20.0 Mpa |
| MD:屈服,23µm,挤塑薄膜 | ASTM D882 | 7.00 Mpa | |
| film thickness | 23 µm | ||
| tensile strength | TD:屈服,23µm,挤塑薄膜 | ASTM D882 | 7.00 Mpa |
| elongation | TD:断裂,23µm,挤塑薄膜 | ASTM D882 | 690 % |
| Basic performance | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| melt mass-flow rate | 190℃/2.16kg | ISO 1133 | 6 g/10min |
| film thickness | 23 um | ||
| density | ASTM D-792 | 0.919 g/m3 |
| Mechanical properties | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| tensile strength | 23um，Cast Film，屈服,TD | ASTM D-882 | 7 Mpa |
| 23um，Cast Film，TD,断裂 | ASTM D-882 | 20 Mpa | |
| elongation at break | 23um，Cast Film，MD | ASTM D-882 | 520 % |
| Elmendorf tear strength | 23um，Cast Film，MD | ASTM D-1922 | 250 g |
| tensile strength | 23um，Cast Film，屈服,MD | ASTM D-882 | 7 Mpa |
| Dart impact | 23um，Cast Film | ASTM D-1709A | 120 g |
| elongation at break | 23um，Cast Film，TD | ASTM D-882 | 690 % |
| Elmendorf tear strength | 23um，Cast Film，TD | ASTM D-1922 | 490 |
| tensile strength | 23um，Cast Film，MD,断裂 | ASTM D-882 | 26 Mpa |
| optical performance | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| gloss | 20°，23um，Cast Film | ASTM D-2457 | 148 |
| Haze ratio | 23.0µm,铸造薄膜 | ASTM D1003 | 0.70 % |
| gloss | 20°,23.0µm,铸造薄膜 | ASTM D2457 | 148 |
| Haze ratio | 23um，Cast Film | ASTM D-1003 | 0.7 % |
| processability | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| Melt Temperature | 220-280 °C |
| physical property | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 6.0 g/10min |
| Thermal performance | Test Condition | Test Method | STYRON US/2035G |
|---|---|---|---|
| vicat | ISO 306/A | 97.0 °C |