Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS FZ-928N DIC JAPAN
DIC.PPS
--
Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DIC JAPAN/FZ-928N |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 650 J/m |
| hardness | Test Condition | Test Method | DIC JAPAN/FZ-928N |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 84 |
| R级 | ASTM D785 | 118 |
| Mechanical properties | Test Condition | Test Method | DIC JAPAN/FZ-928N |
|---|---|---|---|
| elongation at break | ASTM D790 | 3.4 % | |
| Tensile modulus | ASTM D638 | 7500 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.1 % |
| bending strength | ASTM D790 | 180 Mpa | |
| Poisson's ratio | 7.58 0.37 | ||
| coefficient of friction | 与钢-动态 | ASTM D1894 | 0.35 |
| 与钢-静态 | ASTM D1894 | 0.35 | |
| Flexural modulus | ASTM D790 | 6600 Mpa | |
| compressive strength | ASTM D695 | 170 Mpa | |
| tensile strength | ASTM D638 | 135 Mpa |
| Electrical performance | Test Condition | Test Method | DIC JAPAN/FZ-928N |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| Dissipation Factor | 1MHz | ASTM D150 | 2E-03 |
| dielectric constant | 1MHz | ASTM D150 | 4.00 |
| Compared to the Leakage Tracking Index (CTI) | ASTM D3638 | V | |
| dielectric strength | 1.60mm | ASTM D149 | 24 KV/mm |
| arc resistance | ASTM D495 | 120 sec |
| physical property | Test Condition | Test Method | DIC JAPAN/FZ-928N |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.32 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.020 % |
| Shrinkage rate | TD | ASTM D955 | 1.2 % |
| Thermal performance | Test Condition | Test Method | DIC JAPAN/FZ-928N |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 230 °C |
| Linear coefficient of thermal expansion | MD：-30到100°C | ASTM D696 | 3.5E-05 cm/cm/°C |