Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EFR2151HU BK 9001 MITSUBISHI GAS SHANGHAI
IUPILON™ 
Automotive components、Special for cast film
High temperature resistan、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/EFR2151HU BK 9001
Impact strength of simply supported beam without notch23°CISO179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/EFR2151HU BK 9001
Nominal tensile fracture strainISO527-2120 %
Tensile stress屈服ISO527-262.0 Mpa
Bending stressISO17893.0 Mpa
Tensile strain屈服ISO527-26.5 %
Tensile modulusISO527-22300 Mpa
Flexural modulusISO1782500 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/EFR2151HU BK 9001
Surface ResistivityIEC600936E+15 ohms
dielectric strength1.00mmIEC60243-131 KV/mm
Dissipation Factor100HzIEC602506E-04
Relative Permittivity100HzIEC602503.10
1MHzIEC602503.10
Volume resistivityIEC600933E+16 ohms·cm
dielectric strength3.00mmIEC60243-118 KV/mm
Dissipation Factor1MHzIEC602509E-03
flammabilityTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/EFR2151HU BK 9001
UL flame retardant rating1.5mmUL94V-0
physical property Test ConditionTest MethodMITSUBISHI GAS SHANGHAI/EFR2151HU BK 9001
Shrinkage rate吸水率(饱和,23°C)0.24 %
MD:3.20mm0.50to0.70 %
Melt volume flow rate300°C/1.2kgISO113314.0 cm3/10min
melt mass-flow rate300°C/1.2kgISO113315 g/10min
Shrinkage rateTD:3.20mm0.50to0.70 %
Thermal performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/EFR2151HU BK 9001
Heat Deflection Temperature0.45MPa,未退火ISO75-2/B140 °C
1.8MPa,未退火ISO75-2/A126 °C
Linear thermal expansion coefficientMDISO11359-26.5E-05 cm/cm/°C
TDISO11359-26.6E-05 cm/cm/°C