ABS ABS M22 MARPLEX AUSTRALIA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MARPLEX AUSTRALIA/ABS M22 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | 350 J/m |
| Dart impact | 3.20mm | ASTM D3029 | 30.0 J |
| hardness | Test Condition | Test Method | MARPLEX AUSTRALIA/ABS M22 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 102 |
| Mechanical properties | Test Condition | Test Method | MARPLEX AUSTRALIA/ABS M22 |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | 40 % |
| bending strength | 3.20mm | ASTM D790 | 68.0 MPa |
| tensile strength | 3.20mm | ASTM D638 | 41.0 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 2200 MPa |
| flammability | Test Condition | Test Method | MARPLEX AUSTRALIA/ABS M22 |
|---|---|---|---|
| Hot filament ignition temperature | 1.6mm | AS/NZS60695.2.12 | 550 °C |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MARPLEX AUSTRALIA/ABS M22 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.60 % |
| Water absorption rate | 24hr | ASTM D570 | 0.25 % |
| melt mass-flow rate | 230°C/3.8kg | ASTM D1238 | 5.0 g/10min |
| density | ASTM D792 | 1.04 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 19 g/10min |
| Thermal performance | Test Condition | Test Method | MARPLEX AUSTRALIA/ABS M22 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 81.0 °C |
| vicat | ASTM D15254 | 104 °C | |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 87.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 9E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 76.0 °C |