Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1164G-15 TORAY SHENZHEN
Toraycon®
Electrical appliances,Electrical components
Flame retardant,Filler: Glass fiber reinf,15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| BarFlowLength | 250°C,1.00mm | 内部方法 | 150 mm |
| hardness | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 85 |
| Electrical performance | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| dielectric constant | 23°C,50Hz | IEC 60250 | 3.60 |
| 23°C,1kHz | IEC 60250 | 3.80 | |
| dielectric strength | IEC 60243-1 | 14 KV/mm | |
| Volume resistivity | IEC 60093 | 5E+16 ohms·cm | |
| Dissipation Factor | 23°C,50Hz | IEC 60250 | 2E-03 |
| 23°C,1MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Mechanical properties | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| Friction coefficient - vs. Metal | SuzukiMethod | 0.15 | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| bending strength | 23°C | ISO 178 | 160 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 100 Mpa |
| Flexural modulus | 23°C | ISO 178 | 6600 Mpa |
| coefficient of friction | 0.20 | ||
| Tensile modulus | 23°C | ISO 527-2 | 7100 Mpa |
| flammability | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.3 % |
| MD:3.00mm4 | 内部方法 | 0.50 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.070 % |
| Thermal performance | Test Condition | Test Method | TORAY SHENZHEN/1164G-15 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C | |
| Linear coefficient of thermal expansion | MD：-30到100°C | ISO 11359-2 | 5.3E-05 cm/cm/°C |