Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC EXL1414T SABIC INNOVATIVE NANSHA

LEXAN™

Electrical field,Electronic field,Household appliances,Household appliances,Bottle cap

Low temperature resistanc,transparent,Processability,Moderate liquidity,Ductility,copolymer

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
Rockwell hardness	L-Sale	ISO 2039-2	87

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	121 °C
Hot deformation temperature		1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	116 °C
Linear coefficient of thermal expansion	MD:-40to95°C	ASTME831	6.7E-05 cm/cm/°C
		MD:23to80°C	ISO 11359-2	6.7E-05 cm/cm/°C
		TD:-40to95°C	ASTME831	8E-05 cm/cm/°C
		TD:23to80°C	ISO 11359-2	8E-05 cm/cm/°C
RTI		UL 746	130 °C
RTI Elec		UL 746	130 °C
Vicat softening temperature	--	ASTMD152511	139 °C
Vicat softening temperature		--	ISO 306/B50	138 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
Bending modulus	50.0mmSpan5	ASTM D790	2180 Mpa
Bending modulus		--6	ISO 178	2120 Mpa
bending strength	Yield,50.0mmSpan5	ASTM D790	92.0 Mpa
bending strength		--6,7	ISO 178	88.6 Mpa
elongation	Yield	ISO 527-2/50	5.4 %
		Yield4	ASTM D638	5.6 %
		Break4	ASTM D638	120 %
		Break	ISO 527-2/50	110 %
Tensile modulus	--3	ASTM D638	2190 Mpa
Tensile modulus		--	ISO 527-2/1	2310 Mpa
tensile strength	Yield	ISO 527-2/50	56.8 Mpa
		Break	ISO 527-2/50	55.3 Mpa
		Break4	ASTM D638	59.1 Mpa
		Yield4	ASTM D638	57.6 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
Surface resistivity		ASTM D257	>1.0E+15 ohms
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
density		ASTMD792	1.19 g/cm³
melt mass-flow rate	300°C/1.2kg	ASTM D1238	10 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.50 cm3/10min
Shrinkage rate	TD:3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate		MD:3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.093 %
Water absorption rate		Saturation,23°C	ISO 62	0.12 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
Charpy Notched Impact Strength	23°C	ISO 179/1eA	70 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	60 kJ/m²
Dart impact	-30°C,TotalEnergy	ASTM D3763	77.4 J
Dart impact		23°C,TotalEnergy	ASTM D3763	75.5 J
Impact strength of cantilever beam gap	23°C9	ISO 180/1A	65 kJ/m²
		-30°C9	ISO 180/1A	55 kJ/m²
		23°C	ASTM D256	820 J/m
		-30°C	ASTM D256	710 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	无断裂

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature		0.8mm	IEC 60695-2-13	850 °C
UL flame retardant rating	3.0mm	UL 94	V-2
UL flame retardant rating		0.8mm	UL 94	HB

optical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1414T
transmissivity	2540μm	ASTM D1003	82.0 %
turbidity	2540μm	ASTM D1003	3.0 %