Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS OE006 SABIC INNOVATIVE US
LNP™ STAT-KON™
Automotive Applications
Carbon fiber reinforced、High impact resistance、Filler: Carbon fiber rein、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/OE006 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 28 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 1.70 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.2 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 3.30 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/OE006 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 25500 Mpa | |
| bending strength | ASTM D790 | 305 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 210 Mpa |
| 断裂 | ISO 527-2 | 204 Mpa | |
| Wear factor | Washer | ASTM D3702Modified | 857 10^-10in^5-min/ft-lb-hr |
| Flexural modulus | ASTM D790 | 23500 Mpa | |
| Tensile modulus | ASTM D638 | 32800 Mpa | |
| elongation | 断裂 | ASTM D638 | 1.1 % |
| bending strength | ISO 178 | 312 Mpa | |
| coefficient of friction | Static | ASTM D3702Modified | 1.4 |
| Tensile strain | 断裂 | ISO 527-2 | 1.0 % |
| Flexural modulus | ISO 178 | 24700 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 1.6 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/OE006 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+2to1.0E+6 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/OE006 |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/OE006 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.080 % |
| MD：24小时 | ASTM D955 | 0.10 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.020 % |
| 平衡,23°C,50%RH | ISO 62 | 0.030 % | |
| Shrinkage rate | TD：24hr | ASTM D955 | 0.40 % |
| TD:24小时 | ISO 294-4 | 0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/OE006 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 4E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 4.1E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 7.2E-06 cm/cm/°C | |
| MD：-40到40°C | ISO 11359-2 | 8.7E-06 cm/cm/°C |