PA6 Niretan B S25 AE/V0 Soredi S.p.a.
--
--
Filler, glass beads, 25%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -20°C,3.20mm | J/m | 30 40 |
| 23°C,3.20mm | J/m | 40 70 |
| hardness | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| Rockwell hardness | R级 | 95 -- |
| Electrical performance | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| Surface Resistivity | ohms | 1E+14 1E+13 | |
| Volume resistivity | ohms·cm | 1E+15 1E+12 | |
| dielectric strength | 1.00mm | kV/mm | 30 25 |
| relative permittivity | 1MHz | 3.50 4.00 | |
| Dissipation Factor | 1MHz | 0.020 0.10 |
| Mechanical properties | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| Flexural modulus | MPa | 3800 1300 | |
| elongation | 断裂 | % | 4.0 10 |
| tensile strength | 断裂 | MPa | 60.0 45.0 |
| bending strength | 断裂 | MPa | 80.0 -- |
| flammability | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | V-0 -- | |
| 1.6mm | V-0 -- | ||
| Hot filament ignition temperature | 2.0mm | °C | 960 -- |
| physical property | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| Shrinkage rate | MD | % | 0.50to1.2 -- |
| density | g/cm³ | 1.49 -- | |
| Water absorption rate | 平衡,23°C,50%RH | % | 2.5 -- |
| 23°C,24hr | % | 6.0 -- |
| Thermal performance | Test Condition | Test Method | Soredi S.p.a./Niretan B S25 AE/V0 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到55°C | cm/cm/°C | 8E-05 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 65.0 -- |
| Crystallization peak temperature | DSC | °C | 220 -- |