Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 200-3 Trinseo
--
Sheet materials, household goods, electrical appliances
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 960 J/m |
| InstrumentedDartImpact | 23°C,TotalEnergy | ASTM D3763 | 93.8 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | NoBreak |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | NoBreak |
| Impact strength of cantilever beam gap | ASTM D1822 | 630 kJ/m² | |
| 23°C | ISO 180/A | 93 kJ/m² |
| hardness | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 74 |
| R计秤 | ASTM D785 | 118 |
| Electrical performance | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| Dissipation Factor | 60Hz | ASTM D150 | 1E-03 |
| dielectric strength | IEC 60243-1 | 17 kV/mm | |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| Volume resistivity | ASTM D257 | 2E+17 ohms·cm | |
| dielectric strength | ASTM D149 | 17 kV/mm | |
| Dissipation Factor | 1MHz | ASTM D150 | 2E-03 |
| dielectric constant | 1MHz | ASTM D150 | 3.00 |
| Mechanical properties | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 60.0 MPa |
| Flexural modulus | ISO 178 | 2410 MPa | |
| bending strength | ASTM D790 | 96.5 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| bending strength | ISO 178 | 96.0 MPa | |
| Taber abraser | ASTM D1044 | 45 % | |
| elongation | 断裂 | ASTM D638 | 150 % |
| Tensile modulus | ASTM D638 | 2480 MPa | |
| tensile strength | 断裂 | ASTM D638 | 72.4 MPa |
| Flexural modulus | ASTM D790 | 2410 MPa | |
| Tensile modulus | ISO 527-2/50 | 2480 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 150 % |
| tensile strength | 断裂 | ISO 527-2/50 | 72.0 MPa |
| optical performance | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 89.0 % | |
| refractive index | ASTM D542 | 1.586 | |
| Haze ratio | ASTM D1003 | 1.0 % | |
| refractive index | ISO 489 | 1.586 |
| flammability | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Average degree of combustion | ASTM D635 | 3 cm | |
| Limiting Oxygen Index | ISO 4589-2 | 26 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50to0.70 % |
| MD | ISO 294-4 | 0.50to0.70 % | |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| density | ISO 1183/B | 1.20 g/cm³ | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.15 % |
| 平衡,23°C,50%RH | ISO 62 | 0.32 % | |
| 23°C,24hr | ASTM D570 | 0.15 % | |
| density | ASTM D792 | 1.20 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 3.0 g/10min |
| 300°C/1.2kg | ISO 1133 | 3.0 g/10min |
| Thermal performance | Test Condition | Test Method | Trinseo/200-3 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 132 °C |
| 1.8MPa,退火，HDT | ASTM D648 | 143 °C | |
| vicat | ASTM D15256 | 151 °C | |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 143 °C |
| vicat | ISO 306/B50 | 151 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 132 °C |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 146 °C |
| 0.45MPa,退火，HDT | ISO 75-2/B | 146 °C |