Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT S650FR NC010 DUPONT USA
Cristin®
Electronic and electrical
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/S650FR NC010 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 42 kJ/m² |
| 23°C | ISO 180/1U | 45 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| -30°C | ISO 179/1eU | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | DUPONT USA/S650FR NC010 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| Dissipation Factor | 100Hz | IEC 60250 | 7.1E-04 |
| relative permittivity | 1MHz | IEC 60250 | 3.50 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.018 |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/S650FR NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3000 Mpa | |
| Tensile creep modulus | 1hr | ISO 899-1 | 2500 Mpa |
| Nominal tensile fracture strain | ISO 527-2 | 7.2 % | |
| bending strength | ISO 178 | 100 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.6 % |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1800 Mpa |
| tensile strength | 屈服 | ISO 527-2 | 65.0 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/S650FR NC010 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 0.75mm | IEC 60695-11-10,-20 | V-0 | |
| 1.5mm | IEC 60695-11-10,-20 | V-0 | |
| FMVSS flammability | FMVSS302 | DNI | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| physical property | Test Condition | Test Method | DUPONT USA/S650FR NC010 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.6 % |
| MD | ISO 294-4 | 1.8 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.39 % |
| Ejection Temperature | 170 °C | ||
| Shrinkage rate | MD2 | ISO 294-4 | 2.2 % |
| TD2 | ISO 294-4 | 2.2 % | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.15 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/S650FR NC010 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 221 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 160 °C |
| vicat | ISO 306/B50 | 175 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |