Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA LI-941 LG CHEM KOREA
--
Casters、Electric wire、Cable、Electrical appliances、Electronic field、Electrical field、Application in the automo、Automotive External Parts
Weather resistance、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-941
density
ASTMD792
g/cm³
1
density
ISO1183
g/cm³
1
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
6
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
6
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
MD：3.20mm
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-941
FlexuralStrength
6.40mm
ASTMD790
Mpa
7
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
1
Tensile modulus
ISO527-2/1
Mpa
2
tensile strength
屈服,3.20mm
ASTMD638
Mpa
4
tensile strength
屈服
ISO527-2/50
Mpa
4
elongation
断裂,3.20mm
ASTMD638
%
2
Bending modulus
6.40mm
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ISO178
Mpa
7
Impact strength of cantilever beam gap
23°C,6.40mm
ASTMD256
J/m
1
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
1
Thermal performance
Test Condition
Test Method
Unit
ASA/LG CHEM KOREA/LI-941
RTI Imp
UL746
°C
5
RTIElec
UL746
°C
5
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/Ae
°C
8
vicat softening point
ASTMD15256
°C
1
vicat softening point
ISO306/B50
°C
1