PA66 Polytron® A50B01 POLYRAM ISRAEL
--
--
Filler, glass fiber reinforced material, 50%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYRAM ISRAEL/Polytron® A50B01 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 28 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 250 J/m |
| 23°C | ISO 180 | 25 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 100 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYRAM ISRAEL/Polytron® A50B01 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 1.5 % |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ASTM D790 | 16500 MPa | |
| Tensile modulus | ISO 527-2 | 18000 MPa | |
| ASTM D638 | 1800 MPa | ||
| tensile strength | 屈服 | ISO 527-2 | 230 MPa |
| 屈服 | ASTM D638 | 230 MPa | |
| bending strength | ASTM D790 | 380 MPa | |
| Flexural modulus | ISO 178 | 16500 MPa | |
| bending strength | ISO 178 | 380 MPa |
| flammability | Test Condition | Test Method | POLYRAM ISRAEL/Polytron® A50B01 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYRAM ISRAEL/Polytron® A50B01 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.10to0.30 % |
| Water absorption rate | 饱和 | ASTM D570 | 3.4 % |
| Shrinkage rate | ISO 294-4 | 0.10to0.30 % | |
| Water absorption rate | 平衡 | ASTM D570 | 1.0 % |
| 平衡,23°C,50%RH | ISO 62 | 1.0 % | |
| 饱和,23°C | ISO 62 | 3.4 % | |
| density | ASTM D792 | 1.58 g/cm³ | |
| ISO 1183 | 1.58 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYRAM ISRAEL/Polytron® A50B01 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 253 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 253 °C |