Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO FE1520PW-73701 SABIC EU
NORYL™
valve、Faucet、Water pump impeller、shower head
Low water absorption、Hot water resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC EU/FE1520PW-73701
Melt Volume-Flow Rate (MVR)
280°C/10.0kg
ISO1133
cm3/10min
2
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,50%RH
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC EU/FE1520PW-73701
CharpyUnnotchImpactStrength
23°C
ISO179/1eU
kJ/m²
3
Tensile modulus
ASTMD638
Mpa
7
Tensile modulus
ISO527-2/1
Mpa
7
tensile strength
断裂
ASTMD638
Mpa
1
tensile strength
断裂
ISO527-2/5
Mpa
1
Ball pressure hardness
H358/30
ISO2039-1
Mpa
2
elongation
断裂
ASTMD638
%
2
elongation
断裂
ISO527-2/5
%
2
Taber abraser
1000Cycles,1000g,CS-17转轮
内部方法
mg
6
Bending modulus
50.0mm跨距
ASTMD790
Mpa
6
Bending modulus
ISO178
Mpa
6
bending strength
断裂,50.0mm跨距
ASTMD790
Mpa
1
Bending strength 5,
ISO178
Mpa
1
Unscented Izod Impact Strength
-30°C
ISO180/1U
kJ/m²
2
Unscented Izod Impact Strength
23°C
ISO180/1U
kJ/m²
2
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
4
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
6
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC EU/FE1520PW-73701
Hot deformation temperature
0.45MPa,Unannealed,100mmSpan
ISO75-2/Be
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
vicat softening point
--
ISO306/A50
°C
1
vicat softening point
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
7