PA12 Latiohm 82-02 PD09 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Latiohm 82-02 PD09 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.5 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 25 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Latiohm 82-02 PD09 |
|---|---|---|---|
| tensile strength | 屈服,23°C | ISO 527-2/5 | 50.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 50 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 45.0 MPa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2100 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2/5 | 15 % |
| Electrical performance | Test Condition | Test Method | LATI S.p.A./Latiohm 82-02 PD09 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+02 ohms |
| physical property | Test Condition | Test Method | LATI S.p.A./Latiohm 82-02 PD09 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.90to1.1 % |
| density | ISO 1183 | 1.22 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.90to1.2 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Latiohm 82-02 PD09 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C |
| vicat | ISO 306/B50 | 140 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 50.0 °C |