PC 2870-21317 SABIC INNOVATIVE US
LEXAN™
chip、food
high viscosity、Food contact compliance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Vicat Softening Temperature | Rate B/5 | ISO 306 | 149 °C |
| Rate B/5 | ASTM D1525 | 150 °C | |
| Specific Heat | ASTM C 351 | 1.25 J/g-°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Rockwell hardness R | ISO 2039-2 | 120 R |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ISO 1133 | 2 cm³/10 min |
| 300°C/2.16 kg | ISO 1133 | 4 cm³/10 min | |
| Modeling Shrinkage(Across Flow) | flow, 3. | Internal | 0.5~0.7 |
| Moisture Absorption | equilibriu | ASTM D570 | 0.35 |
| 23°C/sat | ISO 62 | 0.35 | |
| Melt Mass-Flow Rate | / | ASTM D1238 | 2.5 g/10min |
| Moisture Absorption | 23°C / 50 | ISO 62 | 0.15 |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Tensile Strength(Yield) | Type I, 5 | ASTM D638 | 62 Mpa |
| Tensile Elongation?(Break) | 50 mm/m | ISO 527 | 70 % |
| Tensile Strength(Yield) | 2 mm/ | ISO 178 | 95 Mpa |
| Tensile Strength(Break) | 50 mm/m | ISO 527 | 70 Mpa |
| Tensile Elongation?(Yield) | 50 mm/m | ISO 527 | 7 % |
| Tensile Elongation?(Break) | Type I, 5 | ASTM D638 | 70 % |
| Flexural Modulus | 2 mm/mi | ISO 178 | 2300 Mpa |
| 1.3 mm/min | ASTM D790 | 2300 Mpa | |
| Tensile Strength(Break) | Type I, 50 | ASTM D638 | 65 Mpa |
| Tensile Elongation?(Yield) | Type I, 5 | ASTM D638 | 7 % |
| Tensile Strength(Yield) | 50 mm/m | ISO 527 | 65 Mpa |
| 1.3 mm/min/ | ASTM D790 | 95 Mpa |
| Optical | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Transmittance | 2.54 mm | ASTM D1003 | 88 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/2870-21317 |
|---|---|---|---|
| Notched Izod Impact Strength (23℃) | 80*10*3 | ISO 180/1U | NB kJ/m² |
| Charpy Notched Impact Strength (23°C) | V-notch Edgew | ISO 179/1eA | 70 kJ/m² |
| Notched Izod Impact Strength 23℃ | ASTM D256 | 750 J/m | |
| Notched Izod Impact Strength (23℃) | 80*10*3 | ISO 180/1A | 75 kJ/m² |
| Charpy Notched Impact Strength (-30°C) | V-notch Edgew | ISO 179/1eA | 50 kJ/m² |
| Gardner Impact | ASTM D 3029 | 170 J | |
| Notched Izod Impact Strength (23℃) | ASTM D 4812 | NB J/m | |
| Notched Izod Impact Strength (-30℃ ) | 80*10*3 | ISO 180/1A | 55 kJ/m² |
| / | ASTM D256 | 150 J/m |