Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPEE 5526 DUPONT TAIWAN
BEXLOY®
Automotive sector、Electrical field、Electronic field、Electrical appliances、Fitness equipment
Thermal stability、High mobility、UV resistance、Weather resistance、currency
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| Tensile impact strength | 23°C | ISO8256/1 | 270 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| 邵氏D | ISO868 | 55 | |
| 邵氏D,15秒 | ISO868 | 51 |
| Supplementary Information | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| Odor | VDA270 | 5.00 |
| Electrical performance | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| 100Hz | IEC60250 | 4.90 | |
| CTI | IEC60112 | 600 V | |
| Dissipation Factor | 100Hz | IEC60250 | 9E-03 |
| Volume resistivity | IEC60093 | 4E+13 ohms·cm | |
| dielectric strength | IEC60243-1 | 20 KV/mm | |
| Dissipation Factor | 1MHz | IEC60250 | 0.038 |
| 1MHz | IEC60250 | 4.60 |
| Mechanical properties | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 170 Mpa |
| Tensile stress | 屈服 | ISO527-2 | 15.0 Mpa |
| 50%应变 | ISO527-2 | 14.0 Mpa | |
| Tensile modulus | ISO527-2 | 190 Mpa | |
| Tensile stress | 5.0%应变 | ISO527-2 | 6.90 Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 130 Mpa |
| Tensile strain | 断裂 | ISO527-2 | >300 % |
| Nominal tensile fracture strain | ISO527-2 | 780 % | |
| Tensile stress | 断裂 | ISO527-2 | 40.0 Mpa |
| 10%应变 | ISO527-2 | 11.0 Mpa | |
| Tensile strain | 屈服 | ISO527-2 | 35 % |
| Flexural modulus | ISO178 | 200 Mpa | |
| abrasion resistance | ISO4649 | 120 mm³ |
| flammability | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL94 | HB |
| 3.0mm | IEC60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | SE/B | |
| Burning rate 3 | 1.00mm | ISO3795 | 28 mm/min |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB |
| 1.5mm | UL94 | HB | |
| Limiting Oxygen Index | ISO4589-2 | 21 % | |
| Fogging-G-value | condensate | ISO6452 | 1E-04 g |
| elastomer | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| tear strength | 横向流量 | ISO34-1 | 130 kN/m |
| 流量 | ISO34-1 | 130 kN/m |
| physical property | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| ThermalConductivityofMelt | 0.19 W/m/K | ||
| Melt volume flow rate | 220°C/2.16kg | ISO1133 | 17.5 cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.4 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.60 % |
| melt mass-flow rate | ISO1133 | 18 g/10min | |
| SpecificHeatCapacity of Melt | 2110 J/kg/°C | ||
| Shrinkage rate | MD | ISO294-4 | 1.4 % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.60 % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % | |
| MediumDensity | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | DUPONT TAIWAN/5526 |
|---|---|---|---|
| MD：-40to23°C | ISO11359-2 | 1.8E-04 cm/cm/°C | |
| 0.45MPa,未退火 | ISO75-2/B | 65.0 °C | |
| TD：-- | ISO11359-2 | 2E-04 cm/cm/°C | |
| 1.8MPa,未退火 | ISO75-2/A | 45.0 °C | |
| Glass transition temperature 2 | ISO11357-2 | -20.0 °C | |
| vicat | -- | ISO306/A50 | 180 °C |
| melting temperature | ISO11357-3 | 203 °C | |
| brittle temperature | ISO974 | -98.0 °C | |
| MD：-- | ISO11359-2 | 2E-04 cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1.7E-04 cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 9E-08 m²/s | |
| vicat | -- | ISO306/B50 | 75.0 °C |