Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM NW-02 DAICEL MALAYSIA
DURACON®
Electrical field、Electronic field、Fitness equipment、Automotive sector、Bottle cap
High sliding、wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| ColorNumber | CF2001/CD3501 |
| hardness | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 70 |
| Mechanical properties | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 11200 kg/cm²(MPa)[Lb/in²] | |
| Wear factor | 0.98MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec7 | JISK7218 | 1000 10^-8mm³/N·m | |
| Tensile modulus | ISO 527-2 | 2350 Mpa | |
| Wear factor | 0.98MPa,0.30m/sec5 | JISK7218 | 19 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec6 | JISK7218 | 300 10^-8mm³/N·m | |
| Flexural modulus | ASTM D790/ISO 178 | 334000 kg/cm²(MPa)[Lb/in²] | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.17 |
| tensile strength | ISO 527-2 | 52.0 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 20 % | |
| bending strength | ISO 178 | 72.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.37 |
| Electrical performance | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 20 KV/mm |
| Surface Resistivity | IEC 60093 | 3E+15 ohms |
| other | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| characteristic | 经润滑 |
| Physical properties | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 |
| flammability | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 18.0 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 2.0 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 20 g/10min |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.8 % |
| Thermal performance | Test Condition | Test Method | DAICEL MALAYSIA/NW-02 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.2E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 85.0 °C |