PC S-3000 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electrical applications,Automotive Applications
Low viscosity,Weather resistance
UL
TDS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/S-3000 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 10 Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 25.2 | |
| Volume resistivity | ASTM D257/IEC 60093 | 2.1-10 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/S-3000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 740-1000 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 80.4-90.2 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2.3 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 90-140 % | |
| Rockwell hardness | ASTM D785 | R122-124 | |
| tensile strength | ASTM D638/ISO 527 | 58.8-68.6 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/S-3000 |
|---|---|---|---|
| characteristic | 低粘度.耐侯性良.脱模性良 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/S-3000 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5-0.8 % | |
| density | ASTM D792/ISO 1183 | 1.2 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 11-14.5 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.23-0.26 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/S-3000 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 6-7 mm/mm.℃ |