Product Name / Manufacturer / Model

Grade

Reference Price

PA66 LANXESS GERMANY D.AKV50H2.0

Injection grade

US$ 3,680 / MT

FOB Guangzhou port, China

film	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Thin film puncture strength	--7	ISO 6603-2	1050 J
Thin film puncture strength		--6	ISO 6603-2	1160 J
Electrical performance	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Dissipation factor	23°C,1MHz	IEC 60250	0.015
Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	40 KV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Surface resistivity		IEC 60093	1E+13 ohms
Relative permittivity	23°C,100Hz	IEC 60250	4.50
Dissipation factor	23°C,100Hz	IEC 60250	9E-03
Relative permittivity	23°C,1MHz	IEC 60250	4.00
thermal performance	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Vicat softening temperature	--	ISO 306/B50	>230 °C
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	8E-05 cm/cm/°C
Ball Pressure Test	258°C	IEC 60695-10-2	Pass
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250 °C
Vicat softening temperature	--	ISO 306/B120	>230 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	261 °C
mechanical properties	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Tensile strain	Break,23°C	ISO 527-2/5	2.6 %
Bending modulus	23°C	ISO 178/A	14000 Mpa
bending strength	23°C	ISO 178	360 Mpa
tensile strength	Break,23°C	ISO 527-2/5	230 Mpa
Tensile modulus	23°C	ISO 527-2/1	16000 Mpa
bending strength	FlexuralStrainatFlexuralStrength5(23°C)		3.0 %
bending strength		3.5%Strain	ISO 178/A	-- Mpa
Physical properties	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Shrinkage rate	TD:300°C,3.00mm2	ISO 2577	0.90 %
Shrinkage rate		MD:120°C,2hr,3.00mm3	ISO 2577	0.020 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.4 %
Shrinkage rate	MD:300°C,3.00mm2	ISO 2577	0.23 %
Water absorption rate	Saturation,23°C	ISO 62	4.0 %
Shrinkage rate	TD:120°C,2hr,3.00mm3	ISO 294-4	0.040 %
Apparent density		ISO 60	0.70 g/cm³
hardness	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Ball Pressure Test		ISO 2039-1	246 Mpa
flammability	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Extreme Oxygen Index		ISO 4589-2	27 %
UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	600 °C
UL flame retardant rating	1.6mm	UL 94	HB
BurningBehavior	>1.00mm	ISO 3795	passed
impact performance	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	95 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	100 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	85 kJ/m²
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	85 kJ/m²
Supplementary Information	Test Condition	Test Method	LANXESS GERMANY/D.AKV50H2.0
ISO Shortcut		ISO 1874	PA66.GHR.14-160.GF50