LLDPE FP120-A NOVA CANADA
SCLAIR®
chip、Plate、Packaging film
high strength、High toughness、Easy to process、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | NOVA CANADA/FP120-A |
|---|---|---|---|
| Low friction puncture | 25.0µm，吹膜 | 内部方法 | 360 J/cm |
| film | Test Condition | Test Method | NOVA CANADA/FP120-A |
|---|---|---|---|
| Secant modulus | 1%正割,MD:25µm,吹塑薄膜 | ASTM D882 | 175 Mpa |
| tensile strength | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 32.0 Mpa |
| Elmendorf tear strength | TD:25µm,吹塑薄膜 | ASTM D1922 | 610 g |
| Secant modulus | 1%正割,TD:25µm,吹塑薄膜 | ASTM D882 | 195 Mpa |
| elongation | TD:断裂,25µm,吹塑薄膜 | ASTM D882 | 670 % |
| Dart impact | 25µm,吹塑薄膜 | ASTM D1709A | 270 g |
| Elmendorf tear strength | MD:25µm,吹塑薄膜 | ASTM D1922 | 420 g |
| tensile strength | MD:屈服,25µm,吹塑薄膜 | ASTM D882 | 10.0 Mpa |
| film thickness | 25 µm | ||
| tensile strength | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 48.0 Mpa |
| elongation | MD:断裂,25µm,吹塑薄膜 | ASTM D882 | 480 % |
| tensile strength | TD:屈服,25µm,吹塑薄膜 | ASTM D882 | 10.0 Mpa |
| optical performance | Test Condition | Test Method | NOVA CANADA/FP120-A |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTM D2457 | 59 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTM D1003 | 10 % |
| physical property | Test Condition | Test Method | NOVA CANADA/FP120-A |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |