PC EXL1112-BR6G177 SABIC INNOVATIVE NANSHA
LEXAN™
Fitness equipment、Bottle cap、Electrical field、Electronic field
High mobility、Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| RTIElec | UL746 | 130 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Vicat Softening Temperature | ASTMD152511 | 144 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 124 °C |
| RTIStr | UL746 | 125 °C | |
| Vicat Softening Temperature | -- | ISO306/B120 | 145 °C |
| Linear thermal expansion coefficient | MD：23到80°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 125 °C |
| 0.45MPa,Annealed | ISO75-2/Be | 136 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 144 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 137 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| Evolution Calendar intelligent importer | UL746 | 120 °C | |
| Linear thermal expansion coefficient | TD：23to80°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| Hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 95.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 17 g/10min |
| Modeling Shrinkage | TD：3.20mm | 内部方法 | 0.40to0.80 % |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 16.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2320 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 55.0 Mpa |
| Tensile Elongation | ASTMD638 | 110 % | |
| Tensile Strain | ISO527-2/50 | 100 % | |
| Tensile Modulus | ISO527-2/1 | 2150 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 58.1 Mpa |
| Flexural Modulus | ISO178 | 2240 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 95.1 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.8 % |
| Tensile Stress | ISO527-2/50 | 57.0 Mpa | |
| Tensile Strain | 5.0 % | ||
| Flexural Strength | ISO178 | 85.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2280 Mpa | |
| Tensile Strength | 断裂 | 58.7 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 20 kJ/m² |
| Charpy Unnotched Impact Strength | ISO179/1eU | NoBreak | |
| Unnotched Izod Impact Strength | ISO180/1U | NoBreak | |
| Charpy Notched Impact Strength | ISO179/1eA | 25 kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 69.6 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 60 kJ/m² |
| Charpy Unnotched Impact Strength | ISO179/1eU | NoBreak | |
| Unnotched Izod Impact Strength | ISO180/1U | NoBreak | |
| Notched Izod Impact Strength | ISO180/1A | 55 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1112-BR6G177 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 875 °C |
| 3.0mm | 875 °C | ||
| Oxygen Index | ISO4589-2 | 32 % | |
| Glow Wire Flammability Index | 0.8mm | IEC60695-2-12 | 850 °C |
| 3.0mm | 960 °C |