Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Polyester, TS Haysite Plastics H900 Haysite Reinforced Plastics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 53 J/m |
| hardness | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| Barcol Hardness | ASTM D2583 | 30 |
| Electrical performance | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.5E+14 ohms·cm | |
| dielectric strength | ASTM D149 | 16 kV/mm | |
| arc resistance | 1.59mm | ASTM D495 | 180 sec |
| Compared to the Leakage Tracking Index (CTI) | 1.59mm | UL 746 | PLC 1 |
| Mechanical properties | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| bending strength | 屈服 | ASTM D790 | 68.9 MPa |
| compressive strength | ASTM D695 | 110 MPa | |
| Flexural modulus | ASTM D790 | 6890 MPa | |
| tensile strength | 屈服 | ASTM D638 | 20.7 MPa |
| flammability | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| UL flame retardant rating | 1.59mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.10to0.20 % |
| Water absorption rate | 24hr | ASTM D570 | 0.070 % |
| density | ASTM D792 | 1.84 g/cm³ |
| Thermal performance | Test Condition | Test Method | Haysite Reinforced Plastics/Haysite Plastics H900 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 204 °C |