Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1007 TORAY JAPAN
Amilan®
Electrical appliances
Low viscosity、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | 无断裂 -- | |
| -40°C | 无断裂 -- |
| hardness | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | 119 | |
| R计秤,80°C | 80 -- |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| Water absorption rate | 23℃，24小时 | ASTM D-570 | 3.5%水｜- % |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 3.8 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | -40°C | MPa | 3800 3600 |
| bending strength | 23°C | MPa | 110 40.0 |
| tensile strength | 23°C | MPa | 80.0 35.0 |
| bending strength | 80°C | MPa | 40.0 25.0 |
| Taber abraser | 1000Cycles | mg | 3.00to4.00 -- |
| tensile strength | 23℃，屈服 | ASTM D-638 | 3.5%水｜350 kg/cm2 |
| bending strength | 23℃ | ASTM D-790 | 3.5%水｜400 kg/cm2 |
| Rockwell hardness | ASTM D785 | 80 | |
| Flexural modulus | 80℃ | ASTM D-790 | 3.5%水｜3000 kg/cm2 |
| Rockwell hardness | 23℃ | ASTM D-785 | 3.5%水｜88 R-标度 |
| compressive strength | 23℃ | ASTM D-695 | 3.5%水｜- kg/cm2 |
| tensile strength | 80°C | MPa | 25.0 20.0 |
| Tensile strain | 断裂,23°C | % | 35 |
| shear strength | 23°C | MPa | 70.0 65.0 |
| shearing strength | 23℃ | ASTM D-732 | 3.5%水｜650 kg/cm2 |
| bending strength | -40°C | 135 MPa | |
| -40℃ | ASTM D-790 | 3.5%水｜1300 kg/cm2 | |
| Flexural modulus | -40℃ | ASTM D-790 | 3.5%水｜37000 kg/cm2 |
| bending strength | 80℃ | ASTM D-790 | 3.5%水｜250 kg/cm2 |
| compression stress | 23°C | MPa | 80.0 -- |
| Flexural modulus | 23℃ | ASTM D-790 | 3.5%水｜8000 kg/cm2 |
| tensile strength | 80℃，屈服 | ASTM D-638 | 3.5%水｜200 kg/cm2 |
| Impact strength of cantilever beam gap | V-缺口1/2，23℃ | 3.5%水｜40 kg.cm/cm | |
| tensile strength | -40°C | 110 MPa | |
| Flexural modulus | 23°C | 2800 MPa | |
| Tensile strain | 屈服,23°C | % | 2.0 -- |
| elongation at break | 23℃ | ASTM D-638 | 3.5%水｜< 200 % |
| tensile strength | -40℃，屈服 | ASTM D-638 | 3.5%水｜1000 kg/cm2 |
| Flexural modulus | 80°C | MPa | 700 300 |
| Rockwell hardness | 80℃ | ASTM D-785 | 3.5%水｜- R-标度 |
| tensile strength | 23℃，断裂 | 3.5%水｜- kg/cm2 | |
| Friction coefficient - vs. Metal | 0.15to0.20 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| Dissipation Factor | 106Hz | ASTM D-150 | 3.5%水｜- |
| dielectric strength | 1/8 | ASTM D-149 | 3.5%水｜- KV/mm |
| Dissipation Factor | 103Hz | ASTM D-150 | 0.06｜- |
| dielectric constant | 103Hz | ASTM D-150 | 3.5%水｜- |
| Compared to the Leakage Traceability Index (CTI) | UL 746 | 3.5%水｜- V | |
| dielectric constant | 106Hz | ASTM D-150 | 3.5%水｜- |
| 23°C,50Hz | 4.10 9.00 | ||
| dielectric strength | kV/mm | 20 -- | |
| Dissipation Factor | 23°C,1MHz | 0.030 0.13 | |
| Volume resistivity | ohms·cm | 1.0E+14-1.0E+15 1.0E+11到1.0E+12 | |
| Dissipation Factor | 23°C,50Hz | 0.070 0.10 | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^12-13 Ω.cm | |
| dielectric constant | 23°C,1kHz | 3.90 8.00 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | V | PLC 0 |
| arc resistance | sec | 120 -- | |
| 1/8 | ASTM D-495 | 3.5%水｜- 秒 | |
| Dissipation Factor | 50Hz | ASTM D-150 | 3.5%水｜- |
| Volume resistivity | ASTM D-257 | 3.5%水｜1011-1012 Ω.cm | |
| dielectric constant | 50Hz | ASTM D-150 | 3.5%水｜- |
| Dissipation Factor | 23°C,1kHz | 0.060 0.11 | |
| dielectric constant | 23°C,1MHz | 3.40 4.50 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.8 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| UL flame retardant rating | 0.79mm | V-2 -- |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| Water absorption rate | 饱和,23°C | % | 11 -- |
| Shrinkage rate | MD：1.00mm3 | % | 0.50-1.0 -- |
| MD：3.00mm4 | % | 1.0-1.6 -- | |
| Taber abraser | 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- mg/1000次 |
| Water absorption rate | 23°C,24hr | % | 1.8 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM1007 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 182 -- |
| thermal conductivity | 3.5%水｜- Kcal/m·hr·℃ | ||
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜8 ×10-5cm/cm/℃ | |
| melting temperature | °C | 225 -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 -- |
| melting temperature | 差示扫描测热计DSC | 225 °C | |
| specific heat | 3.5%水｜- Cal/g·℃ | ||
| Heat distortion temperature | 4.6kg/cm2，HDT | ASTM D-695 | 3.5%水｜- °C |
| specific heat | J/kg/°C | 1900 -- | |
| thermal conductivity | W/m/K | 0.25 -- | |
| UL-94 flame retardant grade | UL 94 | 3.5%水｜- | |
| melting temperature | 225 ℃（℉） |