Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PETG 0603 EASTMAN USA
--
chip、consumables
High mobility、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EASTMAN USA/0603 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -40°C | ASTM D4812 | 无断裂 |
| 23°C | ASTM D4812 | 无断裂 |
| hardness | Test Condition | Test Method | EASTMAN USA/0603 |
|---|---|---|---|
| Rockwell hardness | R级,23°C | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | EASTMAN USA/0603 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 68.0 Mpa |
| Tensile modulus | 23°C | ASTM D638 | 2030 Mpa |
| 23°C | ISO 527-2 | 2000 Mpa | |
| tensile strength | 断裂,23°C | ISO 527-2 | 29.0 Mpa |
| 屈服,23°C | ASTM D638 | 50.0 Mpa | |
| 断裂,23°C | ASTM D638 | 30.0 Mpa | |
| elongation | 屈服,23°C | ISO 527-2 | 4.0 % |
| 断裂,23°C | ISO 527-2 | 200 % | |
| bending strength | 23°C | ISO 178 | 67.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 48.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2100 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 4.4 % |
| Flexural modulus | 23°C | ASTM D790 | 2060 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 180 % |
| optical performance | Test Condition | Test Method | EASTMAN USA/0603 |
|---|---|---|---|
| transmissivity | ASTM D1003 | 90.0 % | |
| Haze ratio | ASTM D1003 | 0.20 % |
| physical property | Test Condition | Test Method | EASTMAN USA/0603 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.20-0.50 % |
| Thermal performance | Test Condition | Test Method | EASTMAN USA/0603 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 62.0 °C |
| 0.45MPa,未退火，HDT | ASTMD648 | 70.0 °C |