Certificates
PBT/ABS B3708 DAICEL JAPAN
NOVALLOY B
--
Low warpage、Glass fiber reinforced、enhance、Filler: Glass fiber reinf、40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DAICEL JAPAN/B3708 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 200 °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 3E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 210 °C |
| 1.8MPa,未退火 | ISO75-2/A | 190 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 8E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 210 °C |
| Physical | Test Condition | Test Method | DAICEL JAPAN/B3708 |
|---|---|---|---|
| Moisture Absorption | 23°C,24hr | ISO62 | 0.15 % |
| Modeling Shrinkage | MD | ASTMD955 | 0.20到0.40 % |
| Mechanical Properties | Test Condition | Test Method | DAICEL JAPAN/B3708 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 11500 Mpa | |
| Tensile Stress | 屈服 | ISO527-2 | 100 Mpa |
| Flexural Stress | ISO178 | 160 Mpa |
| Flammability | Test Condition | Test Method | DAICEL JAPAN/B3708 |
|---|---|---|---|
| Flame Rating | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | DAICEL JAPAN/B3708 |
|---|---|---|---|
| High Amp Arc Ignition | 1.5mm | UL746 | PLC 3 |
| Hot-wire Ignition | 1.50mm | UL746 | 13 sec |
| High Voltage Arc Tracking Rate | 3.00mm | UL746 | 15.0 mm/min |
| Hot-wire Ignition | 1.5mm | UL746 | PLC 4 |
| Comparative Tracking Index | 3.00mm | IEC60112 | 430 V |
| Arc Resistance | 3.00mm | ASTMD495 | PLC 5 |
| High Voltage Arc Tracking Rate | 3.00mm | UL746 | PLC 1 |
| Dielectric Strength | 1.50mm | ASTMD149 | 24 KV/mm |
| Arc Resistance | 3.00mm | ASTMD495 | 124 sec |
| Comparative Tracking Index | 3.00mm | UL746 | PLC 1 |
| High Amp Arc Ignition | 1.50mm | UL746 | 19.0 |