PBT/ASA S4090G6 BASF GERMANY
Ultradur®
Automotive sector、Industrial components、Electronic field、Electrical field、Applied in fields that re、As for the load-bearing p
Aging resistance、Antichemical、Dimensional stability、high strength、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | BASF GERMANY/S4090G6 |
|---|---|---|---|
| Glass Fiber Content | 30 % |
| Basic performance | Test Condition | Test Method | BASF GERMANY/S4090G6 |
|---|---|---|---|
| Water absorption rate | 0.4 % | ||
| melt mass-flow rate | ISO 1133 | 20 cm3/10min | |
| ISO 1133 | 20 cm ³ /10min | ||
| density | ISO 1183 | 1.39 g/cm³ | |
| ISO 1183 | 1.47 g/cm |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/S4090G6 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 59 KJ/m |
| Charpy Notched Impact Strength | 7 kJ/m² | ||
| elongation | 断裂 | ISO 527-1/- 2 | 2.2 % |
| tensile strength | ISO 527-1/-2 | 100 Mpa | |
| bending strength | ISO 178 | 183 Mpa | |
| ball-indentation hardness | ISO 2039-1 | 164 Mpa | |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 9 KJ/m |
| Tensile modulus | ISO 527-1/-2 | 6900 Mpa | |
| 9700 Mpa | |||
| Impact strength of simply supported beam without notch | 23 ℃ | 55 kJ/m² | |
| elongation | 断裂 | 2.5 % |
| processability | Test Condition | Test Method | BASF GERMANY/S4090G6 |
|---|---|---|---|
| Melt Temperature | 250-275 °C | ||
| Temperature | 60-100 °C |
| physical property | Test Condition | Test Method | BASF GERMANY/S4090G6 |
|---|---|---|---|
| Shrinkage rate | 纵向 | 0.1 % | |
| 横向 | 0.75 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/S4090G6 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa，HDT | ISO 75-1/-2 | 210 °C |
| Linear coefficient of thermal expansion | ISO 11359-1/-2 | 0.4 E-4/°C | |
| Heat distortion temperature | 1.80 MPa，HDT | ISO 75-1/-2 | 175 °C |
| combustibility | UL 94 | HB | |
| Heat distortion temperature | 1.80 MPa，HDT | 160 °C |