Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 450Y MH1 TORAY MALAYSIA
Toyolac®
Automotive components,Electronic appliances
transparent,Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY MALAYSIA/450Y MH1 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 190 J/m |
| 23°C,12.7mm | ASTM D256 | 170 J/m |
| hardness | Test Condition | Test Method | TORAY MALAYSIA/450Y MH1 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 111 |
| Mechanical properties | Test Condition | Test Method | TORAY MALAYSIA/450Y MH1 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 46.0 Mpa |
| elongation | 断裂 | ASTM D638 | 26 % |
| bending strength | ISO 178 | 69.0 Mpa | |
| ASTM D790 | 64.0 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 41.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >10 % |
| Flexural modulus | ASTM D790 | 2060 Mpa |
| flammability | Test Condition | Test Method | TORAY MALAYSIA/450Y MH1 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY MALAYSIA/450Y MH1 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.60-0.90 % |
| density | ASTM D792 | 1.07 g/cm³ | |
| ISO 1183 | 1.07 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 4.0 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY MALAYSIA/450Y MH1 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 104 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 98.0 °C |