PA9T G2330 KURARAY JAPAN
Genestar™
Fiber grade
High temperature resistan、Flame retardant、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | KURARAY JAPAN/G2330 |
|---|---|---|---|
| density | 1.68 g/cm | ||
| Water absorption rate | 40 ℃ ， 95 ％相对湿度， 96小时 | 0.9 % | |
| Glass Fiber Content | 33 % | ||
| Shrinkage rate | 流动方向 | 0.1 % |
| Mechanical properties | Test Condition | Test Method | KURARAY JAPAN/G2330 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 222 kg/cm²(MPa)[Lb/in²] | |
| elongation | 断裂 | ASTM D638 | 2.8 % |
| Flexural modulus | ASTM D790/ISO 178 | 11000 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790 | 222 Mpa | |
| Rockwell hardness | ASTM D785 | 125 R | |
| elongation at break | ASTM D638/ISO 527 | 2.8 % | |
| Impact strength of cantilever beam gap | ASTM D256 | 100 J/m | |
| Rockwell hardness | ASTM D785 | 125 | |
| Flexural modulus | ASTM D790 | 11000 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 175 kg/cm²(MPa)[Lb/in²] | |
| ASTM D638 | 175 Mpa |
| Physical properties | Test Condition | Test Method | KURARAY JAPAN/G2330 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.1 % | |
| density | ASTM D792/ISO 1183 | 1.68 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.9 % |
| Thermal performance | Test Condition | Test Method | KURARAY JAPAN/G2330 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Glass Transition Temperature | 125 °C | ||
| combustibility | UL 94 | V-0 | |
| melting temperature | 306 °C | ||
| 306 ℃（℉） |