Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EFR3000 BK MITSUBISHI ENGINEERING JAPAN
IUPILON™
Non specific food
High mobility、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 6.E+15 Ω | |
| dielectric strength | 1.00mm | IEC 60243-1 | 31 KV/mm |
| Volume resistivity | IEC 60093 | 3E+16 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.1 | |
| relative permittivity | 100Hz | IEC 60250 | 3.10 |
| Dissipation Factor | 100Hz | IEC 60250 | 6E-04 |
| dielectric strength | 3.00mm | IEC 60243-1 | 18 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.10 |
| Volume resistivity | ASTM D257/IEC 60093 | 3.E+14 Ω.cm | |
| Surface Resistivity | IEC 60093 | 6E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 9E-03 |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 92 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 2300 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 2500 kg/cm²(MPa)[Lb/in²] | |
| Nominal tensile fracture strain | ISO 527-2 | 67 % | |
| bending strength | ISO 178 | 92.0 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 4.7 % |
| Tensile modulus | ASTM D638/ISO 527 | 2300 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 67 % | |
| tensile strength | 屈服 | ISO 527-2 | 61.0 Mpa |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| characteristic | 非溴非磷阻燃 不透明 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.5 - 0.7 % | |
| density | ASTM D792/ISO 1183 | 1.19 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.24 % |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| process temperature | 260-290 °C | ||
| Dry conditions | 热风干燥 120℃---約4-8小时 | ||
| screw speed | 50-100 rpm | ||
| Temperature | 70-100 °C |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.50-0.70 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 21.0 cm3/10min |
| Shrinkage rate | 吸水率(饱和,23°C) | 0.24 % | |
| MD:3.20mm | 0.50-0.70 % | ||
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/EFR3000 BK |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 (1.0mm) | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 137 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 125 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 6.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.7E-05 cm/cm/°C | |
| ASTM D696/ISO 11359 | 6.6E-05 mm/mm.℃ |