Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 844V TORAY JAPAN
Toyolac®
Industrial machinery、Fitness equipment
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/844V |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 190 J/m |
| 23°C,12.7mm | ASTM D256 | 140 J/m |
| hardness | Test Condition | Test Method | TORAY JAPAN/844V |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/844V |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2600 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 46.0 Mpa |
| elongation | 断裂 | ASTM D638 | >5.0 % |
| bending strength | ISO 178 | 68.0 Mpa | |
| ASTM D790 | 66.0 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 41.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >5.0 % |
| Flexural modulus | ASTM D790 | 2230 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/844V |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | 5VA |
| 2.0mm | UL 94 | 5VB | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/844V |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40-0.70 % |
| density | ASTM D792 | 1.16 g/cm³ | |
| ISO 1183 | 1.17 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 35 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/844V |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 82.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 76.0 °C |