PA612 FS 4104 A SCHULMAN USA
SCHULAMID®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Physical | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Density | ISO 1183/A | 1.01 g/cm³ |
| Mechanical Properties | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1A/1 | 1200 Mpa | |
| Tensile Strength | 断裂 断裂 | ISO 527-2/1A/50 | 40 Mpa |
| Nominal Tensile Strain at Break | ISO 527-2/1A/50 | > 200 % |
| Thermal | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Vicat Softening Temperature | B50 -- | ISO 306 | 100 °C |
| Heat Deflection Temperature | 1.8 MPa，未退火 1.8 MPa，未退火 | ISO 75-2/Af | 55 °C |
| 0.45 MPa，未退火 0.45 MPa，未退火 | ISO 75-2/Bf | 70 °C | |
| Vicat Softening Temperature | A50 -- | ISO 306/A50 | 200 °C |
| Impact Properties | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23℃ 23°C | ISO 179/1eU | No Break |
| -30℃ -30°C | ISO 179/1eU | No Break |
| Flammability | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Flammability level | 1.5 mm 1.5 mm | IEC 60695-11-10, -20 | HB |
| Glow Wire Ignition Temperature | 3 mm 3.0 mm | IEC 60695-2-13 | 750 °C |
| Flammability level | 3.0 mm 3.0 mm | IEC 60695-11-10, -20 | HB |
| Glow Wire Ignition Temperature | 1.5 mm 1.5 mm | IEC 60695-2-13 | 750 °C |
| Burning Rate | ISO 3795 | 30 mm/min | |
| Glow Wire Flammability Index | 3.0 mm 3.0 mm | IEC 60695-2-12 | 725 °C |
| 1.5 mm 1.5 mm | IEC 60695-2-12 | 725 °C |
| Electrical | Test Condition | Test Method | A SCHULMAN USA/FS 4104 |
|---|---|---|---|
| Comparative Tracking Index | 解决方案 A 解决方案 A | IEC 60112 | 550 V |