PC GSH2020LR MITSUBISHI ENGINEERING JAPAN
IUPILON™
Automotive Applications,electrical equipment,Camera applications
Glass fiber reinforced,Filler: Glass fiber reinf,10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2020LR |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 70 kJ/m² |
| thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2020LR |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 132 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 131 °C | |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 5.9E-05 cm/cm/°C |
| MD | ISO 11359-2 | 5E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2020LR |
|---|---|---|---|
| bending strength | ISO 178 | 105 Mpa | |
| flexural modulus | ISO 178 | 2800 Mpa | |
| Tensile modulus | ISO 527-2 | 3300 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 4.6 % |
| tensile strength | 断裂 | ISO 527-2 | 60.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2020LR |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2020LR |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 17 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 15.0 cm3/10min |
| shrinkage rate | MD:3.20mm | 0.30-0.50 % | |
| TD:3.20mm | 0.30-0.50 % | ||
| 吸水率(饱和,23°C) | 0.14 % |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2020LR |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |