LCP V140 CELANESE USA
VECTRA®
Automotive Applications、Home appliance components
Glass fiber reinforced、Liquid crystal polymer/po、40% glass fiber reinforce
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | CELANESE USA/V140 |
|---|---|---|---|
| density | ISO 1183 | 1670 kg/m |
| Electrical performance | Test Condition | Test Method | CELANESE USA/V140 |
|---|---|---|---|
| relative permittivity | 1000Hz | IEC 60250 | 3.70 |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.20 |
| Dielectric loss | 100Hz | IEC 60250 | 0.020 |
| Volume resistivity | IEC 60093 | 1E+12 ohm.m | |
| Compared to the Leakage Traceability Index (CTI) | IEC 60112 | 175 | |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dielectric loss | 1000Hz | IEC 60250 | 0.0050 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/V140 |
|---|---|---|---|
| Flexural modulus | 23℃ | ISO 178 | 16000 Mpa |
| Impact strength of cantilever beam gap | 23℃ | ISO 180/1A | 7.00 KJ/m |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 11.0 KJ/m |
| Tensile modulus | ISO 527-1 | 16000 Mpa | |
| tensile strength | ISO 527-1 | 145 Mpa | |
| elongation | 断裂 | ISO 527-1 | 1.0 % |
| bending strength | 23℃ | ISO 178 | 230 Mpa |
| Rockwell hardness | ISO 2039-2 | 96 M Scale |
| Thermal performance | Test Condition | Test Method | CELANESE USA/V140 |
|---|---|---|---|
| Linear coefficient of thermal expansion | normal | ISO 11359-1 | 0.000021 cm/cm℃ |
| Crystallization peak temperature | 10℃/min | ISO 11357-1 | 280 °C |
| Linear coefficient of thermal expansion | parallel | ISO 11359-1 | 0.000011 cm/cm℃ |
| combustibility | 0.400mm | UL 94 | V-0 |
| Heat distortion temperature | 1.80MPa，HDT | ISO 75-1 | 270 °C |
| combustibility | 1.50mm | UL 94 | V-0 |