Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DF004PSI-GY7G546 SABIC INNOVATIVE KOREA
LNP™ THERMOTUF™
Plastic bag,Electrical appliances,Medical and nursing supplies
Easy to demould,filler,Glass fiber reinforced ma
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/DF004PSI-GY7G546 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 960 J/m |
| 23°C5 | ISO 180/1U | 61 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE KOREA/DF004PSI-GY7G546 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 5510 Mpa |
| elongation | 断裂 | ASTM D638 | 9.5 % |
| bending strength | 断裂, 50.0 mm 跨距 | ASTM D790 | 148 Mpa |
| tensile strength | 断裂 | ASTM D638 | 91.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 6000 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 5510 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE KOREA/DF004PSI-GY7G546 |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.20 % |
| 流量 : 24小时 | ISO 294-4 | 0.20 % | |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.10 % |
| Shrinkage rate | 横向流量 : 24小时 | ISO 294-4 | 0.45 % |
| 横向流动 : 24小时 | ASTM D955 | 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE KOREA/DF004PSI-GY7G546 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 144 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 139 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距5，HDT | ISO 75-2/Af | 142 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE KOREA/DF004PSI-GY7G546 |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 310 to 320 °C | ||
| Temperature at the rear of the barrel | 295 to 305 °C | ||
| Processing (melt) temperature | 305 to 325 °C | ||
| drying temperature | 120 °C | ||
| Temperature at the front of the material cylinder | 320 to 330 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 80 to 110 °C |