Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP 22H2 MX/25 LATI ITALY
LATENE®
--
Filler: Mineral filler、25% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LATI ITALY/22H2 MX/25 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.50 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| elongation at break | 23°C | ISO 527-2 | 6.00 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 25 Mpa |
| Electrical performance | Test Condition | Test Method | LATI ITALY/22H2 MX/25 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 |
| Flame retardancy | Test Condition | Test Method | LATI ITALY/22H2 MX/25 |
|---|---|---|---|
| UL flame retardant rating | Allcolor | UL -94 | HB 3.00mm |
| Allcolor | UL -94 | HB 1.50mm |
| physical property | Test Condition | Test Method | LATI ITALY/22H2 MX/25 |
|---|---|---|---|
| Shrinkage rate | MD2.0mm | ISO 294-4 | 1.25 % |
| TD2.0mm | ISO 294-4 | 1.35 % |
| Thermal performance | Test Condition | Test Method | LATI ITALY/22H2 MX/25 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa未退火，HDT | ISO 75-2/Af | 55 °C |
| vicat | ISO 306/B50 | 95 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 105 °C |