Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI HU1110 SABIC INNOVATIVE US
ULTEM™
Medical devices、Medical and nursing suppl
Middle flow、Biocompatibility、Steam sterilization
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HU1110 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 28.0 J |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 4.0 kJ/m² |
| 23°C | ISO 180/1A | 4.0 kJ/m² | |
| 3.20mm | ASTM D256 | 1900 J/m | |
| Dart impact | 23°C | ASTM D3029 | 23.0 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU1110 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU1110 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3500 Mpa | |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 174 Mpa |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| Tensile strain | 屈服 | ISO 527-2/5 | 6.0 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 3420 Mpa |
| tensile strength | 断裂 | ASTM D638 | 85.0 Mpa |
| 屈服 | ISO 527-2/5 | 110 Mpa | |
| Tensile modulus | ASTM D638 | 3720 Mpa | |
| elongation | 断裂 | ASTM D638 | 70 % |
| bending strength | ISO 178 | 140 Mpa | |
| Flexural modulus | 100mmSpan4 | ASTM D790 | 3720 Mpa |
| ISO 178 | 3300 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2/5 | 60 % |
| bending strength | Yield,100mmSpan4 | ASTM D790 | 165 Mpa |
| tensile strength | 屈服 | ASTM D638 | 110 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HU1110 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | 5VA | |
| 0.71mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HU1110 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50-0.70 % |
| Melt volume flow rate | 360°C/5.0kg | ISO 1133 | 21.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.65 % |
| 饱和,23°C | ISO 62 | 1.2 % | |
| melt mass-flow rate | 337°C/6.6kg | ASTM D1238 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU1110 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 205 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 199 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 5.5E-05 cm/cm/°C |
| TD：-40到40°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 200 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 5.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| vicat | ASTM D152511 | 219 °C | |
| RTI Imp | UL 746 | 170 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 210 °C |
| RTI Str | UL 746 | 170 °C | |
| RTI Elec | UL 746 | 170 °C |