Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 1105-1001 SABIC INNOVATIVE SHANGHAI
XENOY™ 
Household daily necessiti、Electrical applications、Automotive Applications
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/1105-1001
0°CASTM D256720 J/m
-40°C18-40℃ISO 180/1A35 kJ/m²
23°CISO 180/1A63 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA63 kJ/m²
-40°C-40℃ASTM D256370 J/m
23°CASTM D256760 J/m
Charpy Notched Impact Strength-30°CISO 179/1eA48 kJ/m²
-30°CASTM D256490 J/m
ISO 180/1A51 kJ/m²
-20°CASTM D256690 J/m
-10°CASTM D256700 J/m
hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/1105-1001
Shore hardness邵氏DISO 86879
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/1105-1001
--13ISO 17878.9 Mpa
yieldASTM D63848.8 Mpa
ASTM D6384.2 %
--2ASTM D6382020 Mpa
yieldISO 527-2/5052.4 Mpa
Yield, 50.0mm spanASTM D79076.1 Mpa
fractureISO 527-2/5050.5 Mpa
ASTM D63847.4 Mpa
--12ISO 1782020 Mpa
fractureISO 527-2/50120 %
ASTM D638120 %
yieldISO 527-2/504.5 %
50.0mm spanASTM D7901900 Mpa
Fracture bending strainISO 1787.3 %
--1ASTM D6381990 Mpa
Fracture, 50.0mm spanASTM D79074.7 Mpa
physical property Test ConditionTest MethodSABIC INNOVATIVE SHANGHAI/1105-1001
melt mass-flow rate250°C/5.0kgASTMD123816 g/10min
Shrinkage rateMD:3.20mm内部方法0.80-1.0 %
Specific volumeASTM D7921.20 cm³/g
Shrinkage rateTD:3.20mm内部方法0.80-1.0 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/1105-1001
0.45MPa, Unanealed, 6.40mmASTM D648115 °C
0.45MPa, Unanealed, 64.0mm spanISO 75-2/Bf109 °C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af90.2 °C
vicatASTMD1525123 °C
1.8MPa, Unanealed, 6.40mmASTM D64897.0 °C