Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 3412HF-739L SABIC INNOVATIVE NANSHA
LEXAN™
Electrical applications、Automotive Applications、electrical equipment
Glass fiber reinforced、High rigidity、Flame retardant、Filler: Glass fiber reinf、20% filler by weight、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3412HF-739L |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 110 J/m |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 3.39 J |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 530 J/m |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3412HF-739L |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 3450 Mpa | |
| elongation | 断裂 | ASTM D638 | 4.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 157 Mpa |
| tensile strength | 断裂 | ASTM D638 | 107 Mpa |
| 屈服 | ASTM D638 | 100 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 5520 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 165 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3412HF-739L |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3412HF-739L |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20-0.40 % |
| TD：3.20mm | 内部方法 | 0.45-0.65 % | |
| density | ASTM D792 | 1.34 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 8.5 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3412HF-739L |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 142 °C |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI Str | UL 746 | 80.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 138 °C |
| RTI Elec | UL 746 | 80.0 °C |