Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL9300 SABIC INNOVATIVE US
LEXAN™ 
Electronic and Electrical Applications,Aerospace Applications,lens
High mobility,Ductility at low temperat,Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9300
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature0.45MPa,Unannealed,100mmSpanISO 75-2/Be139 °C
1.8MPa,Unannealed,3.20mmASTM D648126 °C
1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af126 °C
0.45MPa,Unannealed,3.20mmASTM D648139 °C
RTI ElecUL 746125 °C
RTI ImpUL 746110 °C
RTI StrUL 746125 °C
Vicat softening temperatureASTM D152511147 °C
--ISO 306/B120147 °C
--ISO 306/B50145 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9300
Bending modulus50.0mmSpanASTM D7902150 Mpa
ISO 1782150 Mpa
bending strengthYield,50.0mmSpanASTM D79086.0 Mpa
ISO 17886.0 Mpa
elongationBreakASTM D638100 %
YieldASTM D6386.0 %
Tensile modulusASTM D6382150 Mpa
ISO 527-2/12150 Mpa
Tensile strainBreakISO 527-2/50100 %
YieldISO 527-2/506.0 %
tensile strengthYieldASTM D63859.0 Mpa
YieldISO 527-2/5059.0 Mpa
BreakISO 527-2/5058.0 Mpa
BreakASTM D63858.0 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9300
Compared to the anti leakage trace indexIEC 60112PLC 2
CTIUL 746PLC 2
High arc combustion indexHAIUL 746PLC 0
Hot wire ignitionHWIUL 746PLC 2
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL9300
densityISO 11831.24 g/cm³
ASTM D7921.24 g/cm³
melt mass-flow rate300°C/1.2kgASTM D12388.0 g/10min
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11337.00 cm3/10min
Outdoor applicabilityUL 746Cf1
Shrinkage rateTD：3.20mmInternal Method0.40-0.80 %
MD：3.20mmInternal Method0.40-0.80 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.050 %
Saturation,23°CISO 620.12 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL9300
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
-30°CISO 179/1eA50 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A50 kJ/m²
23°CISO 180/1A75 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
23°CISO 179/1eUNoBreak
Suspended wall beam without notch impact strength-30°CISO 180/1UNoBreak
23°CISO 180/1UNoBreak
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL9300
Burning wire flammability index1.9mmIEC 60695-2-12960 °C
Hot filament ignition temperature1.0mmIEC 60695-2-13900 °C
UL flame retardant rating2.5mmUL 945VA
2.0mmUL 945VB
0.8mmUL 94V-0