Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT B 4040 G10 BK BASF GERMANY
Ultradur®
Household appliances,Automotive sector
High gloss,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4040 G10 BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 69 kJ/m² |
| 23°C | ISO 179 | 52 kJ/m² |
| thermal performance | Test Condition | Test Method | BASF GERMANY/B 4040 G10 BK |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTM D648 | 220 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 221 °C | |
| 1.8MPa,未退火 | ASTM D648 | 215 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 205 °C | |
| Linear coefficient of thermal expansion | MD | 2.5E-05 cm/cm/°C | |
| melting temperature | ASTM D3418 | 223 °C | |
| ISO 3146 | 223 °C |
| mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4040 G10 BK |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 225 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 1.5 % |
| flexural modulus | 23°C | ASTM D790 | 13600 Mpa |
| 23°C | ISO 178 | 15000 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 16500 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.5 % |
| tensile strength | 断裂,23°C | ISO 527-2 | 155 Mpa |
| 断裂,23°C | ASTM D638 | 140 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4040 G10 BK |
|---|---|---|---|
| dielectric constant | 100Hz | IEC 60250 | 4.00 |
| 1MHz | IEC 60250 | 4.00 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1.2E-03 |
| 1MHz | IEC 60250 | 0.015 | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| volume resistivity | 1.50mm | ASTM D257 | 1E+13 ohms |
| 1.50mm | ASTM D257 | >1.0E+15 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | BASF GERMANY/B 4040 G10 BK |
|---|---|---|---|
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| shrinkage rate | MD：3.18mm | 0.20 % | |
| Viscosity value | 降低的粘度 | ISO 1628 | 97.0 ml/g |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| 平衡,23°C,50%RH | ISO 62 | 0.12 % | |
| 饱和 | ASTM D570 | 0.40 % | |
| 平衡,50%RH | ASTM D570 | 0.12 % |