ABS LG ABS AF366F LG Chem Ltd.
--
TV casing, electrical components
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG Chem Ltd./LG ABS AF366F |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 210 J/m |
| 23°C,6.40mm | ASTM D256 | 160 J/m | |
| -30°C,6.40mm | ASTM D256 | 49 J/m | |
| -30°C,3.20mm | ASTM D256 | 59 J/m |
| hardness | Test Condition | Test Method | LG Chem Ltd./LG ABS AF366F |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Mechanical properties | Test Condition | Test Method | LG Chem Ltd./LG ABS AF366F |
|---|---|---|---|
| Flexural modulus | 6.40mm | ASTM D790 | 2350 MPa |
| elongation | 断裂,3.20mm | ASTM D638 | >20 % |
| 屈服,3.20mm | ASTM D638 | 5.0 % | |
| Tensile modulus | 3.20mm | ASTM D638 | 2160 MPa |
| bending strength | 6.40mm | ASTM D790 | 65.7 MPa |
| tensile strength | 屈服,3.20mm | ASTM D638 | 39.2 MPa |
| flammability | Test Condition | Test Method | LG Chem Ltd./LG ABS AF366F |
|---|---|---|---|
| UL flame retardant rating | 2.5mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 2.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LG Chem Ltd./LG ABS AF366F |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40to0.70 % |
| density | ASTM D792 | 1.19 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 70 g/10min |
| Thermal performance | Test Condition | Test Method | LG Chem Ltd./LG ABS AF366F |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 83.0 °C |
| vicat | ASTM D15256 | 90.0 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 89.0 °C |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C | |
| RTI Elec | UL 746 | 60.0 °C |